Texture evolution of orthorhombic α″ titanium alloy investigated by in situ X-ray diffraction

Résumé

The present paper deals with an in-situ X-ray diffraction analysis during cyclic tensile tests of a fully martensitic Ti-24Nb alloy. Texture evolution of martensite alpha '' phase was followed during loading-unloading cycles. Preferential formation and reverse transformation of particular martensite variants have been observed based on pole figure analysis. The occurrence of the deformation mechanisms for the martensitic Ti-24Nb alloy was also commented by coupling microstructural observations during in-situ experiments and additional cyclic tests followed by heating after each unloading. Through the study of the evolution of the lattice strain, it was found that under loading conditions, the {020} planes exhibit a large tension lattice strain while the {200} planes are subjected to a compression solicitation, which causes the lattice parameters a and c to be shrunk, and b to be elongated.
Fichier principal
Vignette du fichier
Elmay et al. - Texture evolution of orthorhombic α” titanium allo.pdf (1.07 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01438109 , version 1 (13-07-2017)

Identifiants

Citer

W. Elmay, S. Berveiller, E. Patoor, T. Gloriant, F. Prima, et al.. Texture evolution of orthorhombic α″ titanium alloy investigated by in situ X-ray diffraction. Materials Science and Engineering: A, 2017, 679, pp.504-510. ⟨10.1016/j.msea.2016.10.072⟩. ⟨hal-01438109⟩
417 Consultations
209 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More